10.25394/PGS.12217934.v1 Joshua Trevett Dean Joshua Trevett Dean The Kinetics of Thermal Decomposition and Hot-Stage Microscopy of Selected Energetic Cocrystals Purdue University Graduate School 2020 Energetic cocrystal thermal decomposition kinetics analysis Kissinger method Ozawa method Hot-stage microscopy Mechanical Engineering 2020-04-29 20:09:04 Thesis https://hammer.purdue.edu/articles/thesis/The_Kinetics_of_Thermal_Decomposition_and_Hot-Stage_Microscopy_of_Selected_Energetic_Cocrystals/12217934 <p>The thermal decomposition of four energetic cocrystals composed of 4-amino-3,5-dinitropyrazole (ADNP)/diaminofurazan (DAF), 2,4,6-trinitrotoluene (TNT)/ 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane (CL20), 1,3,5,7-tetranitro-1,3,5,7-tetrazacyclooctane (HMX)/CL20, and 1-methyl-3,5-dinitro-1,2,4-triazole (MDNT)/CL20 were studied using simultaneous differential scanning calorimetry (DSC), thermogravimetry analysis (TGA), and hot-stage microscopy. The kinetic parameters of their thermal decomposition reaction were determined using the Kissinger and Ozawa kinetic analysis methods. Each cocrystal’s peak exothermic temperature (decomposition temperature), activation energy, and pre-exponential constant are reported. Furthermore, these parameters from each cocrystal were compared to the same parameters from the corresponding stoichiometric physical mixture in order to identify changes in behavior attributable to the cocrystallization process. For ADNP/DAF, the cocrystal shows an 8% increase in the peak exotherm temperature and a 11-13% decrease in peak activation energy as compared to its physical mixture. For TNT/CL20, this comparison shows a much smaller change in the peak exotherm temperature (<1%) but shows a 5% decrease in activation energy. This cocrystal also experiences phase stabilization—where a phase transition of one or both coformers is omitted from the decomposition process. The HMX/CL20 cocrystal shows a 1% change in the peak exotherm temperature and shows a 2% increase in activation energy. Finally, for MDNT/CL20, this comparison shows nearly a 4% increase and a drastic decrease in peak activation energy by 42-44%. Cocrystallization clearly affects the thermal decomposition and reaction kinetics of these materials, offering the potential to create a hybrid-class of energetic materials which combines the high performance of an energetic material with the safety and insensitivity of another. </p>